Tension band

ABSTRACT

A tension band for suspending a rotatable measuring mechanism is composed of a metal alloy in which the ratio of the number of free electrons to the number of atoms is between about 4.15 to 4.5.

United States Patent 1191 Steinemann Dec. 11, 1973 TENSION BAND [58] Field of Search 148/32, 134; 75/174, [75] Inventor: Samuel G. Steinemann, Liestal, 75/1755 177; 73/432; 324/158; 29/180 Switzerland [56]- R f Ct d e erences 1 e [73] Assignee: Institut Dr. Ing. Reinhard G straumann AG, waldenburg, FORE! N PATENTS OR APPLICATIONS Switzerland 1,183,476 3/1970 Great Britain l48/l3 R [22] Filed: July Z1971 Primary Examiner-Charles N. Lovell 21 APPL 1 0 4 5 Attorney-David Toren et al.

[30] Foreign Application Priority Data 31 b d f ABSTZACT t t bl ens1on an or suspen mg a to a a e measurmg July 17, 19170 Sw1tzerland 10878/70 mechanism is composed of a metal alloy in which the 1 ratio of the number of free electrons to the number of [52] Cl 1 711;;"51 fig? fl atoms is between about 4.15 to 4.5. [51] Int. Cl. C22c 27/00 11 Claims, 2 Drawing Figures "ATFNTEDUEE 1. 1 1975 Fig. 2

INVENTOR' TENSION BAND BACKGROUND INFORMATION AND PRIOR ART Rotatable measuring mechanisms of measuring instruments are customarily mounted on pivots or are suspended by means of straps or tension bands (hereinafter referred to.as tension bands"). Such measuring instruments are, for example, devices for measuring electrical quantities or values, but scales, gyros and the like are also embraced thereby.

Suspension by tension bands is preferred because it results in high precision, satisfactory position independency and insensitivity to impact forces on the instrument.

With a view to achieving a satisfactory suspension by tension bands, a number of requirements has to be fulfilled by the materials from which the tension bands are made. These requirements may be summarized as follows:

a. The material must have a low shear modulus so that the measuring mechanism can operate with small torque;

b. the material must have mechanical strength so that the suspension can be operated under tension which, in turn, assures insensitivity in respect to inclined positions of .the instrument and in respect to vibration and impacts;

c. The material should have a high degree of corrosion resistance;

(1. The elastic after-effects (non-reversibility of torque) should be as small as possible and the torsional moment should be largely independent from temperature fluctuations;

e. In order to produce the bands in an economical manner, the material should have good formability.

The two most important requirements are those listed under a) and b) above and may be expressed by way of a quality factor Q: The torque necessary to twist a rod is proportional to the shear modulus G and to a geometrical form factor; the form factor, in turn, is proportional to the square of the cross-section of the rod. The linear relation between the torque M and the twisting a of a rod may be expressed as follows:

M=(G k PH) 01 mau Q 3 it will be apparent that the two conditions a) and b) above are interrelated and that not the absolute values of and G are decisive, but rather the ratio o' /G.

A number of metals have been proposed for use in tension bands of the indicated kind. The most common metals presently employed for this purpose are alloys of copper-beryllium, bronze, gold, platinum nickel alloys and cobalt-base-alloys. These metals are imparted with considerable mechanical strength by cold working and heat treatment. For these materials the following values for Q are obtained:

TABLE 1 Alloy 0'; G Q kg/mm kg/mm kg/mm Cu-ZBe 100 7000 1.4 Pt-lr /30 110 10200 1.2 Pt-Ni /10 120 7850 1.8 Cobalt Alloy 170 9000 3.2

SUMMARY OF THE INVENTION It is a primary object of the invention to provide tension bands for the indicated purpose which have high mechanical strength and low torque and further meet requirements of corrosion resistance and vanishing elastic after-effects.

It is a further object of the invention to provide such tension bands which can be manufactured in a simple and relatively inexpensive manner.

Generally, it is an object of the invention to improve on the art of suspending rotatable mechanisms of measuring instruments.

Briefly, and in accordance with the invention it has been found that the above objects are superiorly obtained if the tension bands are composed of an alloy in which the ratio e/a of the number of free electrons to the number of atoms is between 4.15 and 4.5.

Particularly suitable for the inventive purpose are alloys on the basis of titanium, zirconium and hafnium, to wit, the transition elements of Group IV of the periodic system. The suitability of titanium, zirconium and hafnium alloys for tension bands appears from the following embodiments. The inventive tension bands are corrosion-resistant and do not exhibit any elastic aftereffects. Furthermore, the shear modulus has an insignificant temperature dependency.

The alloys used for the inventive tension bands may also contain up to 15 atomic percent of non-transition metals, to wit, for example, up to 15 atomic percent of Al, Sn, In, Ga or Cu. (Unless indicated otherwise refers to percent by weight) TABLE 2 Alloy e/a a; G O

13%V, 11%Cr, 3%A1,

remainder Ti 4.27 120 3500 4.1 30% Nb, remainder Zr 4.3 120 2800 5.2 30% V, remainder Ti 4.3 3000 3.3 50% V, remainder Ti 4.5 100 3200 3.1 17% Cr, remainder Ti 4.3 3000 4.0 40% Nb, remainder Ti 4.26 100 2900 3.5 17% Nb, remainder Hf 4.28 110 3500 3.5 15% Mo, remainder Ti 4.26 110 3400 3.6 11% Mn, 6% Sn, rem.Ti 4.30 110 3700 3.3

The mechanical strength, i.e. the elastic limit of the inventive tension bands is substantially similar to that of prior art tension bands. However, the shear modulus of the inventive tension bands is significantly smaller. In this manner, the quality factor of the inventive bands, as compared to the prior art bands made from materials listed in Table l, is significantly increased. The known materials from which tension bands hitherto have been made, have a face-centered cubic crystal structure, while the materials for the inventive tension bands are body-centered cubic. In addition, of course, the electron concentrations are totally different.

The desired values as listed in Table 2 can be obtained, for example, in the following manner:

A. With a commercially available B-titanium alloy consisting of 13 percent of vanadium, 11 percent of chromium, 3 percent of aluminum, the remainder being titanium (atomic percentages are 12 for V, for Cr, 5 for Al): By solution annealing, quenching, cold-working and tempering at 500C, highest mechanical strength properties are obtained. Cold work and the partial phase decomposition (B' into B a combined together are essential B. With an alloy consisting of 30 percent of niobium and the remainder zirconium: By cold working of the annealed and quenched metal and precipitation hardening, at temperatures of 500-700C. The annealed and rapidly cooled metal has a single phase but is in unstable condition, and the precipitation hardening causes structural decomposition. The obtainable strength however, also depends on the presence of dissolved gases, to wit, 0;, N C and the like, the so-called interstitial atoms with an atomic number smaller than 9, which cause dispersion hardening. The amount of interstitial atoms may rise up to 2000 ppm.

C. With titanium-vanadium alloys which are forgeable in the entire 3- range and which are ductile for cold-working. The alloy consisting of 70 percent titanium and 30 percent of vanadium is annealed at about 900C, quenched and then cold-worked. By precipitation hardening at 450C, which results in a partial phase transition, the elasticity limit of 80 kg/mm can be increased to about 100 kg/mm In the annealed metal 0,; is about 40 kg/mm. TiCr alloys have similar properties and are treated by the same manufacturing steps.

The cold-work is conducted so as to obtain the shape of the band. Commonly it consists of drawing and flattening the wire by rolling.

The above examples are concerned with so-called fi-alloys. The annealed metal or at least the quenched metal is present in the body-centered cubic phase and the composition of the alloy is near the limit of the stability range of this B-phase. At lower electron per atom ratios the hexagonal a-phase is the stable phase.

The shear modulus of a cubic single crystal is direction-dependent and may be expressed with the independent shears CP k (C -C and CS =C by the formula:

1/0 =1/cs 2 [l/CP -1/Cs 1 wherein I is the product sum of the direction cosini and indicates the position of the torsion axis relative to the axes of the single crystal. In polycrsytalline metals,-

transition elements at the beginning of this series of the periodic system.

As a general proposition it may be stated that the tension band may be formed from the metal alloys in which the ratio of the number of free electrons to the number of atoms is between about 4.15 to 4.5, by first annealing the alloy at a temperature above 800C, then shaping the alloy into the desired form by cold-working and finally subjecting the shaped metal to a heat treatment at a temperature range of about 300-900C.

The various features of novelty which characterize the invention are pointed out with particularity in the claims annexed to and forming a part of this specification. For a better understanding of the invention, its operating advantages and specific objects attained by its use, reference should be had to the accompanying drawing and descriptive matter in which there is illustrated and described the preferred embodiment of the i n vention.

IN THE DRAWING FIG. 1 represents examples of the polycrystalline alloys TiV, TiCr, TiNb and ZrNb while FIG. 2 is a diagrammatic view of a tension, band employed for suspending a rotatable instrument:

Turning now to FIG. 1, all these alloys have a similar behavior and, for an electron per atom ratio, e/a of 4, is to 4.5, exhibit particularly low shear moduli. The ratio e/a is equal to 1/1002, v a, and is formed by the sum of the products obtained by multiplying the number of outer electrons (v the group in the periodic system) with the concentration, in atomic percent c for each component i. This behavior of the shear modulus is physically to be interpreted as contribution of the itinerant electrons, to wit, of all the electrons outside closed shells which, with their kinetic and electrostatic energy contribute to cohesion of the metallic crystal. It has surprisingly been found that metals of the third, fourth and fifth period and alloys of these metals have similar characteristics which can be exactly indicated by the ratio e/a. Alloys on the basis of titanium with vanadium, chromium, manganese, iron, cobalt, nickel or niobium, molybdenum or tantalum and tungsten (elements which also are referred to as B-formers) yielded in experiments the low shear moduli, if their concentration is adjusted corresponding to their valence. This apparently is interrelated with the mechanical stability of the body centered cubic B-phase i.e., a fundamental physical property. This is the reason why the alloys for the tension bands of the invention are defined not by their strength or their specific weight or their shear modulus or their chemistry, but rather by their ratio e/a.

The high elastic limit which, according to the formula, comes in with its square value in the quality factor, can be obtained by cold-working, which in respect to the production of tension bands is from a practical point of view always usable. High strength may also be obtained by precipitation hardening, by dispersion hardening from the reaction with dissolved gases, so called interstitial atoms and particularly by phase transformation caused by heat treatments. The last mentioned procedure is applicable for the examples of the Ti, 13V llCr 3A], the TiNb the TiCr and Zr 30Nb-alloys. The first two alloy series are unstable after annealing and quenching for e/a values of 4.15 to 4.4 and decompose upon precipitation aging into a [3 phases and the latter two systems remain single phase ,B only in the quenched state for all alloys. The coldworking accelerates the decomposition. For zirconium alloys the mixability is generally very limited, but rapid cooling prevents the transformation.

According to the diagrammatic showing of FIG. 2, the armature of a measuring instrument having a rotatable measuring mechanism is suspended by an inventive tension band 1. The tension band, in turn, is secured to supports 2. The measured value is indicated by an indicator 3 on a scale (not shown).

What is claimed is:

l. A measuring instrument comprising in combination a rotatable measuring mechanism suspended by tension band, said tension band being characterized in that it is composed of a metal alloy in which the ratio of the number of free electrons to the number of atoms is between 4.15 to 4.5;

wherein the main component of the alloy consists of an element from the group consisting of Ti, Zr and Hf.

2. The combination as claimed in claim 1, wherein the alloy contains an amount of non-transition metals, said amount not exceeding atomic percent.

3. The combination as claimed in claim 1, wherein the alloy contains an amount of elements whose atomic number is smaller than 9, said amount not exceeding 2 atomic percent.

4. The combination as claimed in claim 1, wherein the alloy essentially consists of 13 percent of vanadium, 11 percent of chromium, 3 percent of aluminum, the remainder being titanium.

5. The combination as claimed in claim 1, wherein the alloy essentially consists of 20 to 40 atomic percent of niobium, the remainder being zirconium.

6. The combination as claimed in claim 1, wherein the alloy essentially consists of 20 to 40 atomic percent of vanadium, the remainder being titanium.

7. The combination as claimed in claim 1, wherein the alloy essentially consists of 8 to 20 atomic percent of chromium, the remainder being titanium.

8. The combination as claimed in claim 1, wherein the alloy essentially consists of about 17 percent of niobium, the remainder being hafnium.

9. The combination as claimed in claim 1, wherein the sum of the components titanium plus zirconium plus hafnium of the alloy is at least 50 atomic percents.

10. The combination of claim 2, wherein said nontransition metals are A], Sn, In, Ga or Cu.

11. The combination of claim 3, wherein said elements are oxygen, nitrogen or carbon. 

2. The combination as claimed in claim 1, wherein the alloy contains an amount of non-transition metals, said amount not exceeding 15 atomic percent.
 3. The combination as claimed in claim 1, wherein the alloy contains an amount of elements whose atomic number is smaller than 9, said amount not eXceeding 2 atomic percent.
 4. The combination as claimed in claim 1, wherein the alloy essentially consists of 13 percent of vanadium, 11 percent of chromium, 3 percent of aluminum, the remainder being titanium.
 5. The combination as claimed in claim 1, wherein the alloy essentially consists of 20 to 40 atomic percent of niobium, the remainder being zirconium.
 6. The combination as claimed in claim 1, wherein the alloy essentially consists of 20 to 40 atomic percent of vanadium, the remainder being titanium.
 7. The combination as claimed in claim 1, wherein the alloy essentially consists of 8 to 20 atomic percent of chromium, the remainder being titanium.
 8. The combination as claimed in claim 1, wherein the alloy essentially consists of about 17 percent of niobium, the remainder being hafnium.
 9. The combination as claimed in claim 1, wherein the sum of the components titanium plus zirconium plus hafnium of the alloy is at least 50 atomic percents.
 10. The combination of claim 2, wherein said non-transition metals are Al, Sn, In, Ga or Cu.
 11. The combination of claim 3, wherein said elements are oxygen, nitrogen or carbon. 